With so many emerging metal clay enthusiasts just beginning their jewelry making careers, I decided to create a mini dictionary to help them better understand the lingo that goes along with our alchemous tradition. Feel free to distribute this list to your own students, and if you notice that I've missed something - please leave a comment here with the word you think should be added to the list.


A glossary of words and phrases as they apply to Metal Clay
Compiled and Defined by Lora Hart

Alloy – A mixture of two or more metals that are combined to form a new metal, usually to increase strength or provide resistance to corrosion.
Alum - A food grade powder, found in the spice section of the grocery store which is used in pickling recipes. When dissolved in warm water it may also be used to remove oxides and other impurities from metal. See pickle.
Bail – The part of a pendant through which a chain is strung.
Base clay – Metal clays that are not considered precious metals such as bronze, copper, and steel.
Binder – An organic, non-toxic, burnable material that absorbs water and temporarily holds microscopic particles of powdered metal together to form metal clay.
Bronze – A metal alloy usually consisting of 90% copper and 10% tin.
Burnout – The period in a firing cycle when binder incinerates and excess water evaporates.
Cards – Refers to playing cards used as spacers to roll clay to a consistent thickness.
Carve – The process of using a small, sharp blade to incise a design into dry metal clay.
Copper - A pure, unalloyed, reddish-brown metal.
Clay body - Refers to the specific type and brand of metal clay used - such as bronze, rose bronze, copper, white copper, steel, silver, etc. Terminology borrowed from ceramics.
Cutter – A uniquely shaped metal object with sharp edges, such as a cookie cutter, used to cut clay into decorative shapes.
Dehydrate – The process by which metal clay loses water to the atmosphere, becoming dry - either through natural evaporation or with the aid of a heated atmosphere such as a cup warmer or food dehydrator. 
Extruder – A hand held machine that pushes clay through a tube and out a shaped hole or die to form tubes, hinges, bails, and other small elements.
Fine Silver – Pure, unalloyed silver metal. Can be stamped .999.
Fire (v.) – To sinter metal clay in a kiln. Terminology borrowed from ceramics.
Greenware – Metal clay that is formed and dry, but not yet fired. Terminology borrowed from ceramics.
Investment - A plaster-like powder that when mixed with water and allowed to cure, forms a hardened material that will not burn with extreme heat, as in a kiln. Used for casting, in ring molds/plugs and to replicate an implantable (like a cabochon, gemstone or other item) that may not be fired in a kiln. 
Kiln – A type of furnace capable of reaching the high temperatures needed to sinter metal clay, fire ceramics, or flow glass.
Lavender Oil Paste - A user made concoction of pure, essential oil (most often lavender oil) and commercially or home made slip/paste used to create a stickier, stronger joining material. Home made oil paste may be made with any clay body, and may be used with either unfired, or sintered metal clay. Approximately 15 - 25 drops of oil to 15 grams of slip/paste is recommended. Adjust the proportions as needed.
Leather Hard – Unfired metal clay in which the water has almost completely evaporated, leaving the clay slightly flexible, yet still fragile. Terminology borrowed from ceramics.
Lubrication – A thin coating of olive oil, olive oil based balms or other preparations that may be used as a release on tools, textures, hands, and other objects which may come in contact with metal clay.
Metal Clay - A generic term referring to a malleable jewelry making/sculpting material made from microscopic particles of metal, binder, and water.
Needle Tool – See Pin tool.
Paper – A solid, flexible type of unfired fine silver metal clay made with oil instead of water, which is malleable and can be folded, woven or used to cut decorative appliqués. Also known as Sheet.
Paste - A watered down mixture of clay similar in consistency to nail polish, yogurt, or spackle, depending on the amount of viscosity desired. Also referred to as Slip.
Patina - a green, brown, or black coloration on metal formed naturally or hastened with chemicals. Often intentionally applied to replicate an aged or antique appearance.
Pickle - An acidic solution used to remove oxides and other impurities from metal. A mild, non toxic pickle can be made with ordinary Alum and warm water.
Pin Tool – Any thin, pointed, sharp object used to cut shapes in metal clay. Typically a dressmakers pin or needle set into a wooden handle.
PPP’s – Photo Polymer Plates, a UV cured product used with overhead projection film, toner, and a black and white image to create a custom texture stamp.
Precious Metal Clay (PMC) – The brand name of the first silver metal clay manufactured by Mitsubishi Materials. The letters 'pmc' have been used to refer to metal clay in general, much as Kleenex has come to stand in for all facial tissues. But PMC is a brand name, and doesn't refer to the material itself.
Ramp - The rate at which a kiln's temperature rises expressed in degrees per hour. Full ramp is equivalent to approx.1792ºF per hour.
Rehydrate – The process of adding water to make dry or drying metal clay moist and malleable.
Resist - A substance applied as a coating to protect a metal clay surface during some process, for example using wax, nail polish or other material to create a design on dry metal clay in preparation for water etching or fired metal clay prior to the patina process; or the application of a non-burnable dust (investment, soldering board, etc.) between pieces of touching, dry metal clay to prevent bonding during the firing process.
Ring plug -  Also known as a Ring Sizer or Ring Pellet. A cylindrical form made of jeweler's investment that prevents a ring from shrinking beyond the desired size.
Ring Pellet Mold - A mold which is used with jeweler's investment to create standard, ring size plugs. 
Scratch Foam – A low-tech way to create custom texture sheets using Styrofoam and a rounded stylus or ballpoint pen. Introduced to the metal clay community by Wanaree Tanner.
Sheet – A solid, flexible type of unfired metal clay made with oil instead of water, which can be folded, woven or used to cut decorative appliqués. Also known as Paper.
Shrinkage - Refers to the reduction in size of a metal clay item after drying or firing. Metal clay typically shrinks in mass about 1% during the drying process, and anywhere from 8 to 20% during firing depending on the firing schedule and the specific clay body. Metal clay shrinks uniformly in thickness, height, and circumference, unless prevented by a mechanical element - such as a ring plug or kiln shelf.
Sinter – The process by which metal particles coalesce or fuse together metallurgically at high temperatures without melting.
Slats – Refers to colored plastic strips, which correspond to playing card thicknesses and are used to roll clay to a consistent thickness.
Spacers – Refers to any type of flat, calibrated strips used on either side of an amount of clay to roll a consistent thickness.
Slip – A watered down mixture of clay similar in consistency to nail polish, yogurt, or spackle, depending on the amount of viscosity desired. Also referred to as Paste. May be used to complete repairs, or as a decorative material.
Slip Printing - The method of  pushing thick slip through a template onto dry clay to acheive a surface decoration or texture. Also referred to as the stencil process.
Slip Trailing - The method of applying slip in a painterly manner onto dry metal clay to acheive a surface decoration or texture. 
Steel – An alloy of iron, carbon, and possibly other elements.
Stencil - A thin sheet of tape covered cardboard, plastic or metal with a pattern or geometric shape cut into it, used to replicate the design on the surface below with an application of slip or by the use of a pin tool to cut out shapes. May also be used to simply press a design into fresh metal clay.
Sterling Silver – An alloy usually consisting of 92.5% fine silver and 7.5% copper. Can be stamped .925.
Syringe – A specific formulation of metal clay the consistency of cake frosting, inserted into a syringe and used to make repairs or decorate the surface of metal clay items.
Tearaway – A method of creating low profile texture sheets using glossy paper, a copier, toner, black and white graphics, heat and friction. First developed by Gwen Gibson, and introduced to the metal clay community by Celie Fago.
Texture – Anything that can be used to impress a dimensional design into or onto the surface of clay.
Template – A negative shape in a sheet of plastic, card stock or metal that can be used to cut a pattern in clay.
Tissue Blade - A long, flat strip of stiff metal that is sharp on one edge - used to cut straight sections of clay. Originally a pathologist's tool.
Water Etching - The method of selectively removing/eroding dry metal clay in a specific design by use of a resist, sponge and water to achieve a surface decoration or texture. 


Posted by Lora Hart
Artistic Advisor

2 comments:

Anonymous said...

What a great list, Lora! Thanks for the work that went into it. Since I also work with wire, I thought of Argentium Sterling, but don't know if a definition of that would be helpful to others.
Kathy C.

Lora Hart said...

Thanks Kathy. This list defines materials/tools/ideas/words used specifically associated with metal clay. A similar list for wire working, metalsmithing, or beading would also be very beneficial, but not appropriate here. Thanks for the comment though. We love comments. :)